The BASF Ultrafuse PLA PRO1 is a highly versatile tough polylactic acid based filament for FFF printing. This engineering thermoplastic was specially developed to reduce printing time by 30–80% while retaining excellent surface quality and even better mechanical properties than ABS material. The Ultrafuse PLA PRO1 is a highly reliable polymer that ensures print consistency even between colors and batches, allowing you to get predictable results with every print.
While printing with the PLA PRO1 you can adjust print settings to achieve either ultra-fast speed or flawless surface finish depending on your particular requirements. The manufacturer recommends the following print settings for three different scenarios:
Fast print settings
Strong settings
Aesthetics settings
Nozzle temperature
220 ± 10 °C
220 ± 10 °C
210 ± 10 °C
Print speed
120–150 mm/s
40–70 mm/s
≤ 70 mm/s
Bed temperature
60 °C or non-heated bed with tape / glue
60 °C or non-heated bed with tape / glue
60 °C or non-heated bed with tape / glue
Fill density
≥ 20% (higher = stronger)
≥ 20% (higher = stronger)
≥ 20% (higher = stronger)
Bed modification
no, clean glass
no, clean glass
no, clean glass
Fan speed
100%
no
100%
Top / bottom thickness
1.2 mm (thicker = stronger)
1.2 mm (thicker = stronger)
1.2 mm (thicker = stronger)
Layer height
0.1 mm
≤ 0.06 mm (smaller = stronger)
0.1 mm (smaller = better)
Due to its excellent strength, high versatility, and consistency, the BASF Ultrafuse PLA PRO1 is ideal for tooling or jigs and fixtures manufacturing as well as for plenty of other applications in various fields.
Specifications
Print bed temperature: 50–7120 °C
Nozzle temperature: 200–220 °C
Recommended bed surface: Glass, tape at low temperatures
Nozzle diameter: ≥ 0.4 mm
Print speed: 40–150 mm/s
Printed part density: 1250 kg/m³
Tensile strength, ISO 527: 48.0 MPa (XY), 21.8 MPa (ZX)
Elongation at break, ISO 527: 21.9% (XY), 0.9% (ZX)
Young’s modulus, ISO 527: 3166 MPa (XY), 2930 MPa (ZX)
Flexural strength, ISO 178: 92.4 MPa (XY), 99.1 MPa (XZ)
Flexural modulus, ISO 178: 2823 MPa (XY), 2340 MPa (XZ)
Flexural strain at break, ISO 178: 4.3% (XY), 4.4% (XZ)
The BASF Ultrafuse PLA PRO1 1.75 mm 3D printing filament is sold in 0.75 kg spools. It comes vacuum-sealed with desiccant.
Filament Diameter
1.75 mm
Nozzle diameter
≥ 0.4 mm
Print Speed
40–150 mm/s
Available colors
Grey
Color attribute
Solid
Elongation at break, ISO 527
21.9% (XY), 0.9% (ZX)
Flexural modulus, ISO 178
2823 MPa (XY), 2340 MPa (XZ)
Flexural strain at break, ISO 178
4.3% (XY), 4.4% (XZ)
Flexural strength, ISO 178
92.4 MPa (XY), 99.1 MPa (XZ)
Glass transition temperature
63.0 °C
Impact strength Charpy (unnotched), ISO 179-2
20.4 kJ/m² (XY), 18.8 kJ/m² (XZ)
Nozzle temperature
200–220 °C
Print bed temperature
50–7120 °C
Printed part density
1250 kg/m³
Recommended bed surface
Glass, tape at low temperatures
Spool weight
0.75 kg
Tensile strength, ISO 527
48.0 MPa (XY), 21.8 MPa (ZX)
Young’s modulus, ISO 527
3166 MPa (XY), 2930 MPa (ZX)
Tags:
Color:
Filament Size:
Filament Type:
Our mission
Founded in 2013, we have integrated digital manufacturing in over 10,000 businesses. Today we are a team of 80+ 3D printing enthusiasts, geeks and entrepreneurs on a mission to make these technologies accessible to all.
Trusted integrator
In 2018, 3D Print Awards named us the best digital manufacturing integrator. We offer technology and operational consulting to capture growth and achieve excellence in strategy, manufacturing and distribution.
Expert customer service
Deep expertise in 3D printing, 3D scanning, 3D modelling, plastic casting, laser cutting and CNC milling. It comes from delivering 5,000+ projects at our digital manufacturing bureau. We know what we talk about.
Fast response time